Generation of Energy from a Single Fuel Cell Using Synthesized Solid Electrolyte Membrane from Functionalized Polyisoprene/ Carbon Nanotubes

C.A. Idibie; K.J. Awatefe; R.O. Ogboru

doi:10.6000/1929-5995.2018.07.01.2

Authors

C.A. Idibie Department of Chemical Sciences, Edwin Clark University, P.M.B 101, Kiagbodo, Delta State, Nigeria
K.J. Awatefe Department of Chemistry, College of Education, P.M.B 2090 Agbor, Delta State, Nigeria
R.O. Ogboru Research Coordinating Unit, Forestry Research Institute of Nigeria, P.M.B. 5054, Jericho Hills, Ibadan, Oyo state, Nigeria

DOI:

https://doi.org/10.6000/1929-5995.2018.07.01.2

Keywords:

Energy, sulphonation, polyisoprene, carbonanotubes, fuel cell.

Abstract

Study on the electrical energy generated from a single fuel cell using a synthesized solid electrolyte membrane from polyisoprene that was impregnated with carbonanotubes was carried out. The initial functionalization of the polymer yielded an ion exchange capacity (IEC) of 4.04, 7.82, 11.1 and 15.53 mmol/g with their corresponding degrees of sulphonation (DS) of 10.93, 21.1, 30.03 and 42.02 %, respectively. The later but highest DS achieved water uptake of 49.23 wt % and proton conductivities of 4.3 x 10^-3, 1.2 x 10^-3 and 2.6 x 10^-2 S/cm for membrane of thickness 250, 215 and 120 mm, respectively. The performance testing of the membrane in a single fuel cell achieved an open circuit voltage (OCV) of 647.23 mV with the synthesised membrane of 35 wt % catalyst loading, 589.79 mV and 410.48 mV of 25 wt % and 15 wt % catalyst loading, respectively at constant DS (42.02 %). Their corresponding power densities achieved were 68.67, 49.20 and 35.83 Mw/cm², respectively. Thus the functionalization of polyisoprene impregnated with carbon nanotubes through the process of sulphonation with chlorosulphonic acid resulted into the development of solid polymer electrolyte membrane for fuel cell application.

References

Idibie CA, Abdulkareem AS, Pienaar HCvZ, Iyuke SE, vanDyk L. Sulphonation of Polystyrene-Butadiene Rubber with Chlorosulphonic Acid for Proton Exchange Membrane:Kinetic Study. J Appl Polym Sci 2010; 116: 3473-9. DOI: https://doi.org/10.1002/app.31888

Abdulkareem AS, Afolabi AS, Idibie CA, Iyuke SE, Pienaar HCvZc. Development of composite proton exchange membrane from polystyrene butadiene rubber and carbon nanoballs for fuel cell application. Ener Proc 2011; 14: 2026-7. https://doi.org/10.1016/j.egypro.2011.12.1204 DOI: https://doi.org/10.1016/j.egypro.2011.12.1204

Idibie CA. Properties of sulphonated polyisoprene elastomer for possible proton exchange membrane fuel cell. J Chem Soc Nig 2017; 42(2): 76-80.

Shibasaki M, Yachi T, Tatsuo T. A new direct methanol fuel cell with a zigzag folded membrane electrode assembly. J Pow Sources 2005; 145: 477-4. https://doi.org/10.1016/j.jpowsour.2005.01.068 DOI: https://doi.org/10.1016/j.jpowsour.2005.01.068

Gao Y, Gilles PR, Guiver MD, Jian X, Mikhailenko SD, Wang KS. Sulfonation of poly (phthalazinones) with fuming sulfuric acid mixtures for proton exchange membrane materials. J Mem Sci 2003; 227: 39-5. https://doi.org/10.1016/j.memsci.2003.08.020 DOI: https://doi.org/10.1016/j.memsci.2003.08.020

Quan P, Zhou, B, Sobiesiak A, Liu Z. Water behavior in serpentine micro-channel for proton exchange membrane fuel cell. J pow sources 2005; 150: 131-4. https://doi.org/10.1016/j.jpowsour.2005.02.075 DOI: https://doi.org/10.1016/j.jpowsour.2005.02.075

Cheddie D, Munroe N. Review and comparison of approaches to proton exchange membrane fuel cell modelling. J pow sources 2005; 147: 72-4. https://doi.org/10.1016/j.jpowsour.2005.01.003 DOI: https://doi.org/10.1016/j.jpowsour.2005.01.003

Xianguo L. Principles of fuel cells. Taylor and Francis group, LLC: New York, 2006.

Mahr AR, Sadiq A. Modelling of proton exchange membrane fuel cell performance based on semi-empirical equations. J Ren Ener 2005; 30: 1587-9. https://doi.org/10.1016/j.renene.2004.11.015 DOI: https://doi.org/10.1016/j.renene.2004.11.015

Hogarth WH J, Dunize JCD, Lu GO. Solid acid membranes for high temperature (>140oC) proton exchange membranes fuel cells. J Pow Sources 2005; 142: 223-7. https://doi.org/10.1016/j.jpowsour.2004.11.020 DOI: https://doi.org/10.1016/j.jpowsour.2004.11.020

Iyuke SE, Mohammed AB, Kadhum AH, Daud WR, Rachid C. Improved membrane and electrode assemblies for proton conducting membrane fuel cells. J pow sources 2003; 114: 195-2. https://doi.org/10.1016/S0378-7753(03)00016-8 DOI: https://doi.org/10.1016/S0378-7753(03)00016-8

Idibie CA. Synthesis of Moderate Water-Uptake and Low Methanol Permeable Polymer Electrolyte Membrane from Functionalized Polyisoprene Impregnated Carbon Nanotubes. International J Mat Sci Appl 2018; 7(1): 6-2. DOI: https://doi.org/10.11648/j.ijmsa.20180701.12

Bebin P, Caravanier M, Galiano H. Nafion/Clay -SO3H membrane for proton exchange membrane fuel cell application. J Mem Sources 2005; 278, 35-2. DOI: https://doi.org/10.1016/j.memsci.2005.10.042

Sageetha D. Conductivity and solvent uptake of proton exchange membrane based on polystyrene(ethelene-butadiene)polystyrene triblock polymer. Euro polym J 2005; 41: 2644-2. https://doi.org/10.1016/j.eurpolymj.2005.03.018 DOI: https://doi.org/10.1016/j.eurpolymj.2005.03.018

Idibie CA, Abdulkareem AS, Pienaar HCvZ, Iyuke SE, vanDyk L. Synthesis of low methanol permeation polymer electrolyte membrane from polystyrene-butadiene rubber. Polym-plast Technol Eng 2009; 48:11,1121-9. https://doi.org/10.1080/03602550903147254 DOI: https://doi.org/10.1080/03602550903147254

Chaijie S, Yanghua T, Jian LZ, Jiujun Z, Haijiang W, Jun S, Scott M, Jing L, Paul K. PEM fuel cell reaction kinetics in the temperature range of 23 - 120oC. Electroch Acta 2007; 52: 2552-1. https://doi.org/10.1016/j.electacta.2006.09.008 DOI: https://doi.org/10.1016/j.electacta.2006.09.008